The practical consequence is that a wet preform may not produce the same material distribution and degree of orientation as a dry preform under the same blowing conditions. Other tests show that a wet preform has a lower glass-transition temperature than a dry preform. Another important effect is that “moisture acts as a plasticizer, allowing for more stretch.” This was seen in free-blowing tests in which “wet” preforms heated and blown under the same conditions as “dry” preforms produced larger free-blow balloons. Moisture may also retard transmission of infrared energy through the preform sidewall, lengthening the time it takes to heat the interior surface to the same temperature. This matters because, according to PPI, moisture affects preform heating: “Wet preforms absorb more heat under the same process conditions.” Therefore, additional heat may be required to get to the same temperature as a “dry” preform.
Read: Learn About Operating PET Bottle Machines PPI says, “We typically see 3000 ppm preforms after three to six months of moderately humid storage.” Newly made preforms have a moisture content near zero, but after long-term storage and/or exposure to high humidity, preform moisture content can reach upwards of 10,000 ppm. According to PTI’s report, available on its website ( /PTI), the real issue is the direct effects of moisture itself within PET preforms. The problem is not so much the same as what occurs when PET is injection molded without adequate predrying-moisture causes hydrolysis and loss of molecular weight or I.V. The time of year the preforms were injection molded, along with the environmental conditions in which they are kept, will also impact performance.” The older the preform, the more difficult it will be to process so that the container meets performance criteria.
“is that preforms stored three, six or 12 months will each process differently. These preforms were dried under vacuum to get them back to a condition similar to when they were first molded. To get specific answers to the question, PTI studied 2L and 20-oz preforms that were more than a year old. “With amost 40 years of experience in this area, we knew that the longer the preform is stored, the greater the impact on performance-particularly if that preform was stored in a high-humidity environment.” “Our plant-support personnel were frequently being asked what storage duration was acceptable for preforms and what problems can present themselves during longer storage periods,” explains Sumit Mikherjee, chief technology officer of PTI. Proprietary research from PET blow molding consultants PTI shows that PET bottle performance issues may have their root cause in how long preforms are stored and in what environment.
0 kommentar(er)